冲压四大失效模式对照表Stamping Four Major Failure Modes Reference Table

把冲压常见的四类失效（开裂、起皱、回弹、毛刺）做成一张对照表：每类失效对应可观察的现象、根因方向、关键工艺参数与监控频次，配合参数监控表可直接落地到巡检记录，适合冲压车间工艺、模具与质量人员。The four common stamping failures - cracking, wrinkling, springback and burr - arranged into one reference table: each failure maps to observable symptoms, root-cause directions, key process parameters and monitoring frequency. With the parameter monitoring sheet it can be applied directly to inspection records, for stamping plant process, tooling and quality staff.

模板包含什么What is inside

说明Instructions
失效模式对照Failure Mode Comparison
参数监控表Parameter Monitoring Sheet

解决什么问题What it solves

四大失效模式：现象—根因—参数—对策一表打通Four failure modes in one table: symptom, cause, parameter, countermeasure
关键参数监控表，可直接转为车间巡检记录Key parameter monitoring sheet that converts straight into shop-floor inspection records
模具状态与材料批次的影响单独标注Tooling condition and material batch influences are marked separately
适合新项目调试与量产初期问题定位Useful for new project commissioning and issue locating in early mass production

同类模板More templates

M02

注塑件 PFMEA 分析案例Injection-Molded Part PFMEA Case Study

一份可直接对照的注塑件 PFMEA 完整案例：从结构分析、功能分析到失效分析逐层展开，失效原因追到工艺参数层面，并附七步法自查与 AP 判定规则，解决「知道要做 PFMEA，但不知道写成什么样才算合格」的问题。A complete, directly comparable PFMEA case for injection-molded parts: from structure analysis and function analysis through to failure analysis, with failure causes traced down to process parameters, plus a seven-step self-check and AP rating rules - solving the problem of knowing a PFMEA is required but not knowing what a qualified one looks like.

4 个工作表 · .xlsx 查看并下载

M03

焊接工序 PFMEA 案例Welding Process PFMEA Case Study

面向汽车车身与底盘焊接工序的 PFMEA 案例表，把虚焊、焊穿、气孔、变形等典型失效按「后果—原因—现行控制」拆开，失效原因落到电流、电压、焊接时间、夹具定位等可调参数上，可直接作为车间编写 PFMEA 的参照底稿。A PFMEA case form for automotive body and chassis welding stations, breaking typical failures such as weak welding, burn-through, porosity and deformation down into effect, cause and current control. Failure causes are traced to adjustable parameters like current, voltage, weld time and fixture positioning, so it works directly as a reference draft for shop-floor PFMEA.

2 个工作表 · .xlsx 查看并下载

M04

涂装工序 PFMEA 案例Painting Process PFMEA Case Study

涂装工序链长、变量多，常常写成「漆面不好看」这类空话。这份案例把起泡脱落、颗粒异物、流挂、色差、桔皮五类典型失效逐一拆解，原因追到前处理、喷涂参数、烘烤曲线，是涂装车间做 PFMEA 的实战参照。Painting lines are long and rich in variables, so PFMEA easily degrades into remarks that the paint simply does not look good. This case breaks five typical failures - blistering and peeling, foreign particles, sagging, color difference and orange peel - into root causes down to pretreatment, spraying parameters and baking curves, making it a practical reference for painting PFMEA.